KR AH36 hot rolled flat steel, KR AH36 Ocean steel, KR AH36 shipbuilding steel, KR AH36 offshore engineering steel
KR AH36 hot rolled flat steel specifications: 75 × 7-16, 80 × 7-16, 100 × 8-16, 120 × 8-16, 150 × 9-20, 200 × 10-25, 250 × 10-25, 300 × 12-30, 350 × 12-30, 400 × 15-35
KR AH36 hot rolled flat steel, R A36 chemical composition:
Note: Generally speaking CE will be ≤ 0.40%. If the delivery condition is TMPC, the CE will be : ≤ 0.36% (thickness ≤ 50mm),≤0.38%( when the thickness >50-100).
Ceq% =(C+Mn)/6+(Cr+Mo+V)/5+(Ni+Cu)/15.
KR AH36 hot rolled flat steel, R A36 Mechanical Property:
JW steel keeps more than 10,000 tons hot rolled and cold rolled KR AH36 hot rolled flat steel, R A36 shipbuilding steel in stock each month. We can meet our customer’s any quantity request. Based on these stock source, our advantage industry spread into steel process like : cutting ( any size and any shape ) drilling, welding, milling, machining and steel structure.
Email : pandora@steel-jw.com
Skype : pandora.peng
KR AH36 hot rolled flat steel, R A36 chemical composition:
Grade
|
C max
|
Si max
|
Mn
|
P max
|
S max
|
Als min
|
Ti max
|
Cu max
|
Cr
max
|
Ni
max
|
Mo
max
|
Nb
|
V
|
AH36
|
0.18
|
0.50
|
0.90-1.60
|
0.035
|
0.035
|
0.015
|
0.02
|
0.35
|
0.20
|
0.40
|
0.08
|
0.02-0.05
|
0.05-0.10
|
Ceq% =(C+Mn)/6+(Cr+Mo+V)/5+(Ni+Cu)/15.
KR AH36 hot rolled flat steel, R A36 Mechanical Property:
Grade
|
Rm
(MPa)
|
Re(MPa) min
|
A% min
|
Akv/J min
|
||||||
E.T °C
|
Thickness (mm)
|
|||||||||
≤ 50
|
>50-70
|
>70-100
|
||||||||
L
|
C
|
L
|
C
|
L
|
C
|
|||||
R A36
|
490-630
|
355
|
21
|
0
|
34
|
24
|
41
|
27
|
50
|
34
|
JW steel keeps more than 10,000 tons hot rolled and cold rolled KR AH36 hot rolled flat steel, R A36 shipbuilding steel in stock each month. We can meet our customer’s any quantity request. Based on these stock source, our advantage industry spread into steel process like : cutting ( any size and any shape ) drilling, welding, milling, machining and steel structure.